Flow Agent

Type

Chemical Constitution

Effective ingredients %

Performance

Field of Application

Model Addition

%

Silok®

Flow

307

Polysiloxane

polyether

polymer solution

15

1.Leveling, anti-shrinkage.

2. Fullness, feeling.

3. Well compatibility, strong universal property.

1. Universal solvent type of wood finish paint.

2. Suitable for varnish, matte finishing paint.

0.2-0.5

Silok®

Flow

320

Polysiloxane

methyl aryl

polyether

polymer

50

1. Leveling.

2. Suppressing foam.

3. Excellent recoating.

4. Excellent intermiscibility.

1. High gloss wood finishing paint, matte finishing paint.

2. PE, PU, NC primer paint.

0.1-0.5

Silok®

Flow

5100

polysiloxane

alkyl aryl

polymer

100

1. Quickly leveling.

2. Feeling, anti-abrasion.

3. Defoaming.

4. Matte powder directed.

5.  Recoating

1. Wood/furniture matte finishing paint.

Suggest using with 8244 together, performance will be unique.

0.05-0.3

Silok®

Flow

8000

Polysiloxane

polyether

polymer

100

1. Lower surface tension.

2. Substrate wetting, spreading, promote leveling.

3.Doesnt provide slip, can recoating.

4. Pigments wetting, dispersing, anti-flooding.

5. Lower stable foam.

1. Wood primer, finishing paint.

2. Water-based wood paint.

3. UV wood paint.

0.02-0.2

Silok®

Flow

8244

Polysiloxane

polyether polyester ternary polymer

100

1.Excellent anti-shrinkage property.

2. Unique leveling, it has organic silicone and acrylic acid leveling agent performance: quickly prophase leveling and after leveling are all excellent.

3. Especially for sag resistance of large area leveling and facade coating.

4. Higher fullness and smoothness;

5. Well miscibility and recoating of resin.

6. Unstable foam.

1.  Top grade of wood gloss finishing paint.

2. Matte finishing paint.

3. UV wood paint.

4.  Suggest using with 5100 together.

0.1-0.3

Silok®

Flow

8255

Polysiloxane

polyether

polymer solution

50

1. Leveling, feeling, luster.

2.  Anti-shrinkage, anti-fouling.

3.  Well recoating and intermiscibility.

1.  Water-based wood finishing paint.

0.1-1.0

Silok®

Flow

8266

Polysiloxane

polyether

polymer

100

1. Leveling, luster.

2. Excellent intermiscibility.

3. Unstable foam.

4. High cost performance.

5. Well surface smoothness.

1. PU high gloss finishing paint, varnish.

0.1-0.5